Impurities shouldn't increase resistance unless you have no supercondting path between your probes. If you don't, other tests will be hardly conclusive either.

And yeah, you want the equipment sensitive enough to see that it is better than good metal like copper, which may be nontrivial in case your critical current is low.

After that, you can move on to other measurements